When civil engineering demands a grout that performs, regardless of cold, damp, or heavy-duty conditions, Megapoxy 206 Ultra delivers. This two-component, hydrophilic, water-displacing epoxy grout ensures critical infrastructure remains stable and secure. It offers superior compressive and impact strength, providing reliable adhesion and cure where other materials falter.
Megapoxy 206 Ultra was specifically engineered for the demanding world of civil engineering. It’s a 100% solids, solvent-free, resin-based grout designed to handle high compressive and impact loads. Its hydrophilic nature and ability to displace water allows it to adhere and cure effectively even in adverse, damp environments, ensuring robust and long-lasting bonds in critical applications.
Megapoxy 206 Ultra comes in pre-metered kits, simplifying the mixing process. The mixing ratio is critical: 5 parts A to 1 part B by volume. Thoroughly mix the two parts for a full three minutes, scraping the pail's sides to ensure homogeneity. Incomplete mixing compromises performance. The work time is 30 minutes at 25°C, requiring immediate application after mixing. For cleaning tools and implements, use Megapoxy Thinners Epoxy.
In critical applications like Rail System Installation, Megapoxy 206 Ultra typically serves as a foundational adhesive. It's often the first step in assembling systems such as the Delkor Rail System, applied directly to prepared concrete or steel substrates to form the high-strength bond that supports the entire rail structure. This position in the sequence is vital for ensuring long-term stability and load-bearing capacity.
Unlike conventional grouts or general-purpose epoxies, Megapoxy 206 Ultra is a solvent-free, hydrophilic water displacing, flowable epoxy grout specifically engineered for heavy-duty civil engineering applications. It provides high compressive and impact strength superior to concrete, adheres and cures effectively even in cold or damp conditions, and maintains excellent strength retention after prolonged water immersion. This specialised formulation goes beyond simply filling gaps or providing basic adhesion, offering a robust solution for critical infrastructure where performance cannot be compromised.
Yes, Megapoxy 206 Ultra complies with AS/NZS 4020:2005 for products used in contact with drinking water. This makes it suitable for potable water infrastructure applications where compliance is critical.
The maximum recommended single pour depth is 50mm. For applications requiring greater depths, it is necessary to consult Megapoxy technical services for specific guidance.
Yes, it is formulated to adhere and cure effectively under adverse conditions, including cold and damp environments. The minimum application temperature is 10°C, and it exhibits good strength retention even after prolonged water immersion.
Drill a hole approximately 1.5 times the steel diameter. Blow out dust with oil-free compressed air. Ensure the steel is grit blasted and degreased for optimal bond, then pour from one side to release air.
No, it is strongly recommended to remove all coatings before bonding. Bonding to coated surfaces will result in significantly inferior bond strengths and may lead to product failure.
| Application | Key benefit | Primary trades |
|---|---|---|
| Pile splicing and repair | Develops 115MPa compressive strength, ensuring high structural integrity and longevity, even in damp conditions. | Civil contractors, structural engineers |
| Machinery grouting and backing crusher parts | Provides high compressive (115MPa) and impact strength for heavy machinery, reducing wear and vibration. | Industrial engineers, mechanical fitters |
| Setting anchor bolts and locking PT cables | Achieves >150kN pull-out strength for 25mm rebar, providing reliable anchoring and secure post-tensioning. | Structural engineers, concreters |
| Bridge bearing pads and rail track grouting | Offers strong bond to concrete and steel (>9.5MPa), maintaining critical alignments and resisting dynamic loads. | Rail infrastructure, civil contractors |
| Core hole filling and floor repairs | Superior to concrete with 28MPa tensile strength and 80 Shore D hardness, resisting heavy traffic and chemical attack. | Concreters, maintenance crews |
| Contact with drinking water infrastructure | AS/NZS 4020:2005 compliance ensures suitability and safety for potable water applications. | Civil infrastructure, water treatment specialists |
Ensure all concrete is clean, sound, and mechanically abraded to remove laitance. Steel must be grit blasted or ground to bright metal and degreased. Erect and seal all formwork.
The pre-metered kits are designed for simple and accurate mixing. Do not alter mix ratios.
Add the entire contents of Part B into the Part A container. Using a low-speed mechanical stirrer (200rpm or less), mix for 2 minutes. Scrape the sides and base with a straight edge, then mix for 1 more minute until uniform.
The mixed grout must be applied immediately. Pour from one side of the formwork to allow air to escape from the other side.
Pour the grout continuously until the void is filled. The flowable consistency will ensure it self-levels and fills the entire space.
DANGER
Wear safety shoes, protective clothing, nitrile rubber gloves, safety glasses, and a suitable respirator. Contaminated work clothing must not leave the workplace. Always wash hands thoroughly after handling, before eating, drinking, or using the toilet.
Ensure adequate ventilation to keep air concentrations below exposure standards. Use in well-ventilated areas, with local exhaust ventilation or an appropriate respirator. Prevent vapour concentration in hollows or sumps.
Store in a cool, dry, well-ventilated place, out of direct sunlight and away from foodstuffs, incompatible materials, and sources of heat/ignition. Store locked up with containers closed and upright. Dispose of material and containers in accordance with local, regional, national, and international regulations. Part A is Class 9 Dangerous Goods, Part B is Class 8 Corrosive.
Proper surface preparation is crucial for Megapoxy 206 Ultra to achieve its documented performance, ensuring long-term bond strength and structural integrity.
Surface prep: Remove all grease and oil with an industrial heavy-duty degreaser. Mechanically abrade the surface using scabbling, grit blasting, or grinding to remove surface laitance. If mechanical methods are not possible, acid etching can be performed using a 1:1 mixture of concentrated hydrochloric acid and water, spread at 0.5 L/m². Allow to react for 10 minutes, then wash thoroughly and scrub. Allow 24 hours to dry. Concrete must be surface dry for maximum adhesion.
Primer: Not required for prepared concrete.
Surface prep: Grit blast to AS 1627.2.2002. If grit blasting is not possible, mechanically abrade to a clean, bright metal finish. Degrease the abraded surface by flooding with an industrial-grade degreaser. Wire brushing alone is not sufficient for optimal adhesion.
Primer: Not required for prepared metal.
Surface prep: All existing coatings must be removed entirely. For concrete, this involves flame-cleaning or mechanical scutching, followed by diamond grinding or scabbling. For metals, use a quality paint stripper, then grit blast or grind to a bright metal finish, ensuring all paint and galvanising are removed.
Primer: Not required after complete coating removal and substrate preparation.
| Property | Value |
|---|---|
| Mixing Ratio by Volume | 5 Part A to 1 Part B |
| Work Time at 25°C | 30 minutes |
| Minimum Cure Time at 15°C | 48 hours |
| Minimum Cure Time at 25°C | 24 hours |
| Minimum Cure Time at 35°C | 12 hours |
| Minimum Application Temperature | 10°C |
| Viscosity Part A at 25°C | 45000 - 55000 cps |
| Viscosity Part B at 25°C | 75-90 cps |
| Mixed Viscosity at 25°C | 10000 cps |
| S.G. Part A at 25°C | 1.60 - 1.70 |
| S.G. Part B at 25°C | 0.97 - 0.99 |
| Mixed S.G. at 25°C | 1.54 |
| Colour Part A | Grey |
| Colour Part B | Black |
| Appearance Mixed | Grey |
| Ultimate Compressive Strength - ASTM C579 | 115 MPa |
| Yield Compressive Strength - ASTM C579 | 95 MPa |
| Bond Strength Concrete - ASTM D4541 | >3 MPa |
| Tensile Bond Strength Steel - ASTM D897 | 9.5 MPa |
| Modulus of Elasticity - ASTM C579 | 3 GPa |
| Flexural Strength - ASTM D790 | 60 MPa |
| Tensile Strength ASTM D638 | 28 MPa |
| Tensile Lap Shear Strength - ASTM D1002 | 8 MPa (steel to steel) |
| Hardness - Shore D - ASTM D2240-00 | 80 |
| Dielectric Strength (kV/mm) | 58 |
| Surface Resistivity (Ohm) - ASTM D257 | 10¹² |
| Volume Resistivity (Ohm.cm) | 5.1x10¹⁰ |
| Peak Exotherm Temp - ASTM D2471 | 93.7°C (415ml) |
| VOC (g/l) - ASTM D3960 | 3 |
| Water Vapour Transmission - ASTM E96/E96M | 0.095 (gram/hr m²) |
| Water Absorption - ASTM D570 | 0.066 Increase in weight (%) |
| Minimum Grout Depth | 5 mm |
| Maximum Grout Depth | 50 mm |